標題 | High performance bio-based bismaleimide resins using succinic acid and eugenol |
執筆形態 | 共著 |
掲載誌名 | Polymer Journal |
掲載区分 | 国外 |
出版社・発行元 | Nature Publishing Group |
巻・号・頁 | 43(11),pp.916-922 |
著者・共著者 | Mitsuhiro Shibata, Naozumi Teramoto, Toshiaki Shimasaki, Megumi Ogihara |
概要 | Biseugenyl succinate (BEUS) and bis(4-maleimidephenyl) succinate (BMIS) were synthesized by the reaction of succinic acid with eugenol and the reaction of succinyl chloride with 4-hydroxyphenylmaleimide, respectively. A gelated mixture of BEUS and BMIS in a molar ratio of 1/1, 1/2 or 1/3 at 200 degree C was compression-molded at 230 degree C for 1 h to give a cured BEUS/BMIS product. The properties of BEUS/BMIS were compared with those of 2,2'-diallylbisphenol A (DABA) / 4,4'-bismaleimidediphenylmethane (BMIM) cured at 230 degree C for 1 h. The FT-IR analysis of the cured materials revealed that chain polymerization of ally and maleimide groups proceeds for BEUS/BMIS, while stepwise ene reaction and subsequent chain polymerization in addition to etherification reaction proceed for DABA/BMIM. The cured BEUS/BMIS (1/2, 1/3) showed a higher glass transition temperature and tensile strength than the corresponding DABA/BMIM. |
DOI | 10.1038/pj.2011.87 |
ISSN | 0032-3896 |