標題 | Preparation and properties of biocomposites composed of glycerol-based epoxy resins, tannic acid, and wood flour |
執筆形態 | 共著 |
掲載誌名 | Journal of Applied Polymer Science |
掲載区分 | 国外 |
出版社・発行元 | John Wiley & Sons |
巻・号・頁 | 118(5),pp.2998-3004 |
著者・共著者 | Mitsuhiro Shibata, Naozumi Teramoto, Yoshiro Takada, S. Yoshihara |
概要 | After polyglycerol polyglycidyl ether (PGPE) and glycerol polyglycidyl ether (GPE) were mixed with tannic acid (TA) in ethanol and without solvent, the obtained GPE-TA and PGPE-TA solutions were mixed with wood flour (WF), pre-polymerized, and compressed at 160 degree C. The storage moduli of the biocomposites in the rubbery state were much higher than that of the control cured resins. The PGPE-TA/WF composites had higher tensile modulus and rather lower tensile strength than PGPE-TA. On the other hand, both the tensile modulus and strength of GPE-TA/WF were much higher than those of GPE-TA. Those values of GPE-TA/WF increased with WF content, became maximal values at WF content 60 wt%. FE-SEM analysis of the fractured surface of the biocomposites revealed that WF is tightly incorporated into the crosslinked epoxy resins. The composite with WF content 60 wt% prepared at the epoxy/hydroxy molar ratio of 1/0.8 showed the highest tensile modulus and strength. |
DOI | 10.1002/app.32695 |
ISSN | 0021-8995 |